J.C. Suits, T.R. McGuire, et al.
IEEE Transactions on Magnetics
Faraday rotation and absorption measurements were made on a bulk single crystal and on evaporated polycrystalline films of EuSe. Bulk EuSe is ferromagnetic, transparent in the red, and exhibits an unusually large Verdet constant at room temperature: -9.7 min/Oe-cm at 6660 Å where the absorption is 173 cm-1. Measurements at 77°K show that the Verdet constant varies approximately inversely with temperature and thereby correlates with the magnetic susceptibility. These properties are due to the Eu + + ion and are comparable to those we have observed in other divalent europium compounds such as Eu2SiO4. The evaporated films of EuSe exhibit a broad but well-defined absorption band at 4600 Å which is essentially duplicated in similarly prepared films of EuS and EuO at 5200 and 5800 Å, respectively. The wavelength dependence of the Faraday rotation of EuSe exhibits a rather complicated structure with two sign reversals in the region of the absorption band. At 6660 Å the Verdet constant measured at room temperature is -6.3 min/Oe-cm agreeing in sign and approximately in magnitude with the bulk value, whereas the maximum value of Verdet constant, +25 min/Oe-cm, occurs at 4330 Å. © 1965 The American Institute of Physics.
J.C. Suits, T.R. McGuire, et al.
IEEE Transactions on Magnetics
B.E. Argyle
ECS Meeting 1989
J.C. Suits
Review of Scientific Instruments
J.C. Suits, B.E. Argyle
Physical Review Letters