Imide-aryl ether benzoxazole random copolymers

Novel imide-aryl ether benzoxazole copolymers were prepared and their morphology and mechanical properties investigated. A key feature of these copolymers is the incorporation of a benzoxazole moiety by the use of 2,2′-bis[4-(3-aminophenoxy)phenyl]-6,6′-bibenzoxazole or 2,2′-bis[4-(4-aminophenoxy)-phenyl]-6,6′-bibenzoxazole as co-diamines in polyimide syntheses. The preparation of these diamines involved the nucleophilic aromatic substitution of 2,2′-bis(4-fluorophenyl)-6,6′-bibenzoxazole with either 3- or 4-aminophenol in the presence of K2CO3. The diamines were co-reacted with various compositions of pyromellitic dianhydride (PMDA) and 4,4′-oxydianiline (ODA) to synthesize the desired poly(amic acids). Films were cast and cured (350°C) to effect the imide formation, affording films with elongations between 40 and 110% and moduli in the 2000-2750 MPa range. The copolymers exhibited good dimensional (Tg in excess of 300°C) and thermal stability. Wide-angle X-ray diffraction measurements on the copolymers showed that the ordered morphology characteristic of PMDA/ODA polyimide was retained. Improvements in the auto-adhesion were observed, particularly in those copolymers which displayed a Tg. © 1990.