About cookies on this site Our websites require some cookies to function properly (required). In addition, other cookies may be used with your consent to analyze site usage, improve the user experience and for advertising. For more information, please review your options. By visiting our website, you agree to our processing of information as described in IBM’sprivacy statement. To provide a smooth navigation, your cookie preferences will be shared across the IBM web domains listed here.
Paper
Electromigration failure due to interfacial diffusion in fine Al alloy lines
Abstract
Damage formation at grain boundary junctions has long been recognized as the dominant electromigration failure mechanism in metal lines. We report the results of drift-velocity experiments on fine lines with no reservoirs and find that the interfacial mass transport, along the edges of the lines, is faster than that along grain boundaries. This causes mass depletion at the cathode end of the line, leading to electromigration failure. The result demonstrates a new failure mechanism due to electromigration in submicron lines with bamboo grain structures.