About cookies on this site Our websites require some cookies to function properly (required). In addition, other cookies may be used with your consent to analyze site usage, improve the user experience and for advertising. For more information, please review your options. By visiting our website, you agree to our processing of information as described in IBM’sprivacy statement. To provide a smooth navigation, your cookie preferences will be shared across the IBM web domains listed here.
Paper
Effects of silver and gold on the YBaCuO superconducting thin films with the use of Ag/Cu/BaO/Y2O3 and Au/Cu/BaO/Y 2O3 structures
Abstract
Superconducting YBaCuO films have been fabricated from the Ag/Cu/BaO/Y 2O3 and Au/Cu/BaO/Y2O3 layer structures on MgO substrates. Compared to those using only the Cu/BaO/Y 2O3 structure, the addition of a silver layer to the starting structures improves the film resistances, especially at reduced annealing temperatures, allowing the study of the dependence of the superconducting transition on the annealing temperatures between 900 and 750 °C. Zero resistance is observed at 80 K for the Ag/Cu/BaO/Y 2O3 structure annealed at 900 °C. The use of a gold layer, on the other hand, reduces the temperature for zero resistance to 75 K for a similarly annealed film. All the superconducting films are composed of the YBa2Cu3O7 and the Y2BaCuO 7 phases, with starting compositions off that of the former. Structural and morphological analysis of the films is performed to explore the roles of silver and gold in the films formed.