Corrosive inorganic contamination on wafer surfaces after nickel-iron electroplating formation mechanisms and prevention

Abstract

Electroplating of Nickel-Iron alloys is widely used in the production of magnetic heads for storage systems. Usually, the plating process is performed in acidic, salt-containing solutions. After the plating step, a complete removal of the plating salts is necessary to receive a clean surface. In disadvantageous cases, a precipitation of sticky particles is observed that cannot be removed from the plated surface without damaging the surface. Some of these substances (esp. nickel sulfates) might lead to severe local corrosion and thus might act as "time-bomb" in the later product. Non-corrosive precipitations (i.e. nickel hydroxides) strongly hinder or even prevent the following production steps. In the present paper, the mechanisms of the origin of the different kinds of precipitation are described and the principle actions for their prevention are given. An outlook is given for other possible technical applications. © WILEY-VCH Verlag GmbH, 2001.