I.K. Pour, D.J. Krajnovich, et al.
SPIE Optical Materials for High Average Power Lasers 1992
This paper reports on the electron paramagnetic resonance angular variation of the S = 1 2Cr5+ center with orthorhombic symmetry, obtained after quenching Al and Cr-doped SrTiO3 from 1400 °C. At 4.2 K, the main axes of the g-tensor in monodomain {001} samples are found to be along [001] and rotated by ± α = 2φ{symbol} = 4° from 〈110〉 axes, where φ{symbol} is the intrinsic structural phase transition (SPT) order paramater. From this and the size of the g-values as well as stereometrical considerations, an assignment of the small Cr5+ ion to a tetrahedral site in the perovskite structure is made. Above the tetragonal-to-cubic SPT at Tc = 105 K, a dynamic reorientation among the six equivalent sites is observed, and below Tc, a deviation from α(T) = 2φ{symbol}(T) between 70 K < T < Tc. © 1993.
I.K. Pour, D.J. Krajnovich, et al.
SPIE Optical Materials for High Average Power Lasers 1992
Fernando Marianno, Wang Zhou, et al.
INFORMS 2021
E. Babich, J. Paraszczak, et al.
Microelectronic Engineering
Elizabeth A. Sholler, Frederick M. Meyer, et al.
SPIE AeroSense 1997