About cookies on this site Our websites require some cookies to function properly (required). In addition, other cookies may be used with your consent to analyze site usage, improve the user experience and for advertising. For more information, please review your options. By visiting our website, you agree to our processing of information as described in IBM’sprivacy statement. To provide a smooth navigation, your cookie preferences will be shared across the IBM web domains listed here.
Conference paper
Stress gradients observed in Cu thin films induced by capping layers
Abstract
Glancing-incidence X-ray diffraction (GIXRD) has been applied to the investigation of depth-dependent stress distributions within electroplated Cu films due to overlying capping layers. 0.65 μm thick Cu films plated on conventional barrier and seed layers received a CVD SiCxN yHz cap, an electrolessly-deposited CoWP layer, or a CoWP layer followed by a SiCxNyHz cap. GIXRD and conventional X-ray diffraction measurements revealed that strain gradients were created in Cu films possessing a SiCxNyHz cap, where a greater in-plane tensile stress was generated near the film / cap interface. The constraint imposed by the SiCxNyH z layer during cooling from the cap deposition temperature led to an increase in the in-plane stress of approximately 180 MPa from the value measured in the bulk Cu. However, Cu films possessing a CoWP cap without a SiC xNyHz layer did not exhibit depth-dependent stress distributions. Because the CoWP capping deposition temperature was much lower than that employed in SiCxNyHz deposition, the Cu experienced elastic deformation during the capping process. Cross-sectional transmission electron microscopy indicated that the top surface of the Cu films exhibited extrusions near grain boundaries for the samples undergoing the thermal excursion during SiCxNyH zdeposition. The conformai nature of these caps confirmed that the morphological changes of the Cu film surface occurred prior to capping and are a consequence of the thermal excursions associated with cap deposition. © 2009 Materials Research Society.