Reduction of macroscopic moment in ultrathin Fe films as the magnetic orientation changes

Download paper

Abstract

A study of the remanent magnetization Mr in ultrathin Fe films grown at 125 K on Cu(100) and Ag(100) substrates was conducted using spin-polarized secondary-electron spectroscopy. For bcc-Fe/Ag(100) and fcc-Fe/Cu(100) films, perpendicular Mr was observed for film thickness less than 7 and 11, respectively. In-plane Mr was observed for thicker films. For thickness below the critical thickness, both systems showed a reversible switching transition of the magnetization orientation from perpendicular to in plane as the temperature was increased. For the Fe/Cu(100) films the switching could be observed for many temperature cycles providing that the film was not annealed above 350 K, while the Fe/Ag(100) films switching was stable for only 12 annealing cycles to 300 K. A loss of Mr during the switching transition is observed, and is attributed to a change in the magnetic nature of the film. The details of the loss of magnetization observed in Fe/Ag(100) and Fe/Cu(100) are significantly different. © 1992 The American Physical Society.

Date

Publication

Physical Review B

Authors

Topics

Resources

Share