About cookies on this site Our websites require some cookies to function properly (required). In addition, other cookies may be used with your consent to analyze site usage, improve the user experience and for advertising. For more information, please review your options. By visiting our website, you agree to our processing of information as described in IBM’sprivacy statement. To provide a smooth navigation, your cookie preferences will be shared across the IBM web domains listed here.
Publication
MRS Spring Meeting 2009
Conference paper
Improving silicon crystallinity by grain reorientation annealing
Abstract
Demand for high efficiency, low-cost solar cells has led to strong interest in post-deposition processing techniques that can improve the crystallinity of thick (1 to 40 μm) silicon films deposited at high growth rates. Here we describe a high temperature grain reorientation annealing process that enables the conversion of polycrystalline silicon (poly-Si) into a single crystal material having the orientation of an underlying single crystal Si seed layer. Poly-Si films of thickness 0.5 to 1.0 μm were deposited by low pressure chemical vapor deposition (LPCVD) on substrates comprising a surface thermal oxide or a 100-oriented single crystal silicon-on-insulator (SOI) layer. After annealing at 1300 °C for 1 hour, poly-Si on oxide shows very significant grain growth, as expected. In contrast, the poly-Si deposited on SOI showed no grain boundaries after annealing, transforming into a single crystal material with a fairly high density of stacking faults. Possible uses and drawbacks of this approach for solar cell applications will be discussed. © 2009 Materials Research Society.