Crystallization characteristics of Ge-Sb phase change materials

Abstract

The crystallization behavior of Ge-Sb phase change materials with variable Ge:Sb ratio X between 0.079 and 4.3 was studied using time-resolved x-ray diffraction, differential scanning calorimetry, x-ray reflectivity, optical reflectivity and resistivity vs. temperature measurements. It was found that the crystallization temperature increases with Ge content from about 130 °C for X = 0.079 to about 450 °C for X = 4.3. For low X, Sb x-ray diffraction peaks occurred during a heating ramp at lower temperature than Ge diffraction peaks. For X = 1.44 and higher, Sb and Ge peaks occurred at the same temperature. Mass density change upon crystallization and optical and electrical contrast between the phases show a maximum for the eutectic alloy with X = 0.17. The large change in materials properties with composition allows tailoring of the crystallization properties for specific application requirements. © 2009 Materials Research Society.